1.5519冷鐓冷擠壓用合金鋼棒
發(fā)布者：
yhjs999 發(fā)布時(shí)間：2024-01-04 09:47:45 訪問(wèn)次數(shù)：47
|
牌號(hào)
|
1.5519冷鐓冷擠壓用合金鋼棒
|
|
|
|
|
|
|
|
|
|
|
|
|
歐標(biāo)鋼號(hào)
|
7MnB8
|
|
|
|
|
|
|
|
|
|
|
|
|
對(duì)應(yīng)標(biāo)準(zhǔn)
|
EN 10263-2-2017
|
|
|
|
|
|
|
|
|
|
|
|
|
盤(pán)條，棒材和線材冷鐓和冷擠壓 鋼- 第2部分：冷加工后的交貨技術(shù)條件不適用于熱處理鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
Steel rod,bars and wire for cold heading and cold extrusion - Part 2: Technical delivery conditions for steels not intended for heat treatment after cold working
|
|
|
|
|
|
|
|
|
|
|
|
|
歸類(lèi)
|
合金鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
標(biāo)簽
|
非熱處理鋼
|
|
|
|
|
|
|
|
|
|
|
|
|
1.5519化學(xué)元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Mo
|
Ti
|
V
|
B
|
Al *
|
|
最小值
|
0.06
|
0.15
|
1.85
|
-
|
-
|
-
|
-
|
-
|
0.06
|
0.03
|
0.0015
|
0.02
|
|
最大值
|
0.09
|
0.25
|
1.95
|
0.015
|
0.025
|
0.2
|
0.25
|
0.05
|
0.1
|
0.05
|
0.003
|
0.04
|
|
* 鋁含量可以使用其它可以起到相同作用的元素替代。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
鋼號(hào)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
1.5519機(jī)械性能
|
|
|
|
|
|
|
|
|
|
|
|
|
|
條件
|
熱處理或狀態(tài)
|
抗拉強(qiáng)度
|
斷面收縮率
|
|
|
|
|
|
|
|
|
|
|
σb
|
ψ
|
|
|
|
|
|
|
|
|
|
|
Mpa
|
%
|
|
|
|
|
|
|
|
|
|
|
盤(pán)條,鋼棒；5＜d≤10
|
熱軋或未處理及去皮(+U或+U+PE)
|
≥650
|
≥60
|
|
|
|
|
|
|
|
|
|
|
盤(pán)條,鋼棒；10＜d≤40
|
熱軋或未處理及去皮(+U或+U+PE)
|
≥600
|
≥55
|
|
|
|
|
|
|
|
|
|
|
鋼棒,鋼絲；5＜d≤40
|
未處理及冷拔（+U+C)
|
≥800
|
|
|
|
|
|
|
|
|
|
|