薄壁阻燃性PPO NORYL Resin N1150
PPO 基礎(chǔ)創(chuàng)新塑料(上海) N1150
NORYL Resin N1150
產(chǎn)品說明：
PPE+PS，尺寸穩(wěn)定,低翹曲.絕緣.良好的流動性.無溴.阻燃.薄壁部件應(yīng)用。改性聚苯醚N1150是一個未填充，注入可塑改性聚苯醚樹脂。設(shè)計良好的尺寸穩(wěn)定性和良好的流,該樹脂還使用non-chlorinated,non-brominated FR添加劑達到UL94評級為0.75 mm,我們特定的密度為1.11克/厘米^ 3。改性聚苯醚1150可能是一個優(yōu)秀的候選材料應(yīng)用程序需要電絕緣性能、低吸濕、低翹曲,薄壁阻燃性。
物性數(shù)據(jù)：
溶指15，收縮率0.5-0.7%，吸水率0.07-0.25%，沖擊強度6，熱變形溫度109-108℃，維卡軟化溫度132-130℃，表面電阻率2.0E+16ohm，體積電阻率5.0E+16ohm.cm，加工熔體溫度260-288℃。
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 50 mm/min | 760 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 560 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 8 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 27500 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1190 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 31100 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, yield, 50 mm/min | 72 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 52 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 3.5 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 7 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2650 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 105 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2600 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 8 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, notched, -30°C | 6 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 407 | cm-kgf | ASTM D 3763 | |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 4 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m2 | ISO 179/1eA | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 130 | °C | ASTM D 1525 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 108 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 5.45E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 5.75E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 5.45E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 5.75E-05 | 1/°C | ISO 11359-2 | |
| Vicat Softening Temp, Rate B/50 | 130 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 132 | °C | ISO 306 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 109 | °C | ISO 75/Af | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.11 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method | |
| Melt Flow Rate, 280°C/5.0 kgf | 15 | g/10 min | ASTM D 1238 | |
| Density | 1.11 | g/cm3 | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.07 | % | ISO 62 | |
| Melt Volume Rate, MVR at 280°C/5.0 kg | 15 | cm3/10 min | ISO 1133 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.75 | mm | UL 94 | |