Hanwha Total PP BI970
高結(jié)晶性聚丙烯
HANWHA TOTAL PETROCHEMICALS Co., Ltd.
產(chǎn)品說(shuō)明:
BI970 is a highly isotactic block copolymer with ultra-high flowability, high impact, and higher crystalinity compared to general PP. It maintains an optimum balance of strength and impact resistance due to high crystalline technology and the most appropriate rubber design. Through the control of molecular weight distribution, the product shows superior melt flow compared to normal PP and is appropriate for energy savings and multi-cavity injection molding. BI970 is useful in large scale thin products with low distortion tendencies and may also be used as a compound base resin.
特性 | · Block Copolymer· 高強(qiáng)度· 間苯二甲· 結(jié)晶· 抗撞擊性，高· 流動(dòng)性高· 耐低溫沖擊· 耐熱性，高· 窄分子量分布
|
用途 | · 薄膜· 杯子· 汽車(chē)防撞桿· 汽車(chē)內(nèi)部裝備· 汽車(chē)儀表板· 容器
|
形式 | · 粒子 |
加工方法 | · 注射成型 |
物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
密度 | 0.910 | g/cm3 | ASTM D1505 |
熔流率（熔體流動(dòng)速率） (230°C/2.16 kg) | 100 | g/10 min | ASTM D1238 |
硬度 | 額定值 | 單位制 | 測(cè)試方法 |
洛氏硬度 (R 級(jí)) | 87 | ASTM D785 |
機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
抗張強(qiáng)度 (屈服) | 31.4 | MPa | ASTM D638 |
伸長(zhǎng)率 (斷裂) | 25 | % | ASTM D638 |
彎曲模量 | 1670 | MPa | ASTM D790 |
沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
懸壁梁缺口沖擊強(qiáng)度 (23°C) | 59 | J/m | ASTM D256 |
熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
載荷下熱變形溫度 (0.45 MPa, 未退火) | 125 | °C | ASTM D648 |
光學(xué)性能 | 額定值 | 測(cè)試方法 | |
光澤度 | 85 | ASTM D2457 |
注射 | 額定值 | 單位制 | |
料筒后部溫度 | 160 到 200 | °C | |
料筒中部溫度 | 200 到 240 | °C | |
料筒前部溫度 | 220 到 260 | °C | |
模具溫度 | 30.0 到 50.0 | °C | |
注塑壓力 | 98.1 到 245 | MPa | |
保壓 | 78.5 到 226 | MPa |